Delamination Analysis of Laminated Glass with Polyvinyl Butyral PVB
Interlayer Film
By www.helloglass.com Condition One: Delamination Appears in Lines.
Reason:
When combining the glass with the Polyvinyl Butyral PVB interlayer
film, some folds occur , or some place of Polyvinyl Butyral PVB
interlayer film is too thin due to the hard pulling of the Polyvinyl
Butyral PVB interlayer film. Especially the place near the hole or
edges, some Polyvinyl Butyral PVB interlayer film have been shrink,
so the Polyvinyl Butyral PVB interlayer film is too thin or even gone
between the too glasses. Solution:
When combining the glass with Polyvinyl Butyral PVB interlayer film,
pull the Polyvinyl Butyral PVB interlayer film gently, make sure no
fold of Polyvinyl Butyral PVB interlayer film, and the Polyvinyl
Butyral PVB interlayer film is 2mm wider than the glass. And also cut
the Polyvinyl Butyral PVB interlayer film gently. Condition Two: Delamination in Edges and Holes of Laminated Glass with
Polyvinyl Butyral PVB Interlayer Film
Reason:
The plainness of the edges and holes of the tempered glass is not good. Solution:
Adjust the plainness of the tempered glass, clip the edges of the
pre-laminated glass before putted into the autoclave. But don’t use
too big clips, in case the PVB Film’s shape changes. Condition Three: Delamination on Edges and Holes After the Laminated
Glass is Installed in the Building Solution: Install the laminated glass gently. it’s better if use the
wrench with scale to hole the laminated glass. Make sure the glass
glue is suitable for the laminated glass, and it should be neutral
glue. Condition Four: Irregular Delamination of Laminated Glass with
Polyvinyl Butyral PVB Interlayer Film
Reason1:
The Adhesion of Polyvinyl Butyral PVB interlayer film and glass is not strong.
Solution1:
The washing glass water is not good quality, it’s better use the water
whose electric conductivity is lower than 20us. Solution2:
The Polyvinyl Butyral PVB interlayer film absorbed too much moisture,
maybe more than 6%. If moisture of Polyvinyl Butyral PVB interlayer
film is higher than 1%, the laminated glass may appear white haze. Solution3:
The combination of pre-laminated glass and roller exhausting air stage
maybe not operate correctly, which lead to Polyvinyl Butyral PVB
interlayer film not reacted perfectly. The main parameters are
temperature, pressure and time. Solution4：
The glass surface is not clean and dry enough. Reason2:
The Polyvinyl Butyral PVB interlayer film is too thin.
Solution:
Use thicker or more layer of Polyvinyl Butyral PVB interlayer film. Reason3:
The plainness of the tempered glass is not good.
Solution: Choose better quality tempered glass. Condition Five: Delamination of Laminated Glass with Polyvinyl Butyral
PVB Interlayer Film When in Boling Water Test Reason1:
Two much air contained inside the laminated glass with Polyvinyl
Butyral PVB interlayer film.
Solution1:
Sealing the edges too early in the pre-pressure exhausting air stage,
which lead to the air stocked inside the laminated glass. Although, it
seams successful when the laminated glass come out from the autoclave,
but when in the boiling test, the bubbles will appears.
Reason2:
The Polyvinyl Butyral PVB interlayer film has absorbed too much
moisture before laminating.
Solution2:
Adjust the storage conditions, make sure the moisture of Polyvinyl
Butyral PVB interlayer film is less than 0.55%. Copyright: All rights reserved by CNC-INTERLAYER TECH:
【1】CNC-Force® EVA INERLAYER FOR ARCHITECTURAL LAMINATED GLASS
【2】CNC-Smart® SMART FILM FOR PRIVACY SWITCHABLE GLASS
【3】CNC-Shield® PVB INTERLAYER FOR AUTOMOTIVE WINDSHIELD GLASS
Mail: [email protected]
Web: www.CNCnext.com
[email protected]/
[email protected] 
Interlayer Film
By www.helloglass.com Condition One: Delamination Appears in Lines.
Reason:
When combining the glass with the Polyvinyl Butyral PVB interlayer
film, some folds occur , or some place of Polyvinyl Butyral PVB
interlayer film is too thin due to the hard pulling of the Polyvinyl
Butyral PVB interlayer film. Especially the place near the hole or
edges, some Polyvinyl Butyral PVB interlayer film have been shrink,
so the Polyvinyl Butyral PVB interlayer film is too thin or even gone
between the too glasses. Solution:
When combining the glass with Polyvinyl Butyral PVB interlayer film,
pull the Polyvinyl Butyral PVB interlayer film gently, make sure no
fold of Polyvinyl Butyral PVB interlayer film, and the Polyvinyl
Butyral PVB interlayer film is 2mm wider than the glass. And also cut
the Polyvinyl Butyral PVB interlayer film gently. Condition Two: Delamination in Edges and Holes of Laminated Glass with
Polyvinyl Butyral PVB Interlayer Film
Reason:
The plainness of the edges and holes of the tempered glass is not good. Solution:
Adjust the plainness of the tempered glass, clip the edges of the
pre-laminated glass before putted into the autoclave. But don’t use
too big clips, in case the PVB Film’s shape changes. Condition Three: Delamination on Edges and Holes After the Laminated
Glass is Installed in the Building Solution: Install the laminated glass gently. it’s better if use the
wrench with scale to hole the laminated glass. Make sure the glass
glue is suitable for the laminated glass, and it should be neutral
glue. Condition Four: Irregular Delamination of Laminated Glass with
Polyvinyl Butyral PVB Interlayer Film
Reason1:
The Adhesion of Polyvinyl Butyral PVB interlayer film and glass is not strong.
Solution1:
The washing glass water is not good quality, it’s better use the water
whose electric conductivity is lower than 20us. Solution2:
The Polyvinyl Butyral PVB interlayer film absorbed too much moisture,
maybe more than 6%. If moisture of Polyvinyl Butyral PVB interlayer
film is higher than 1%, the laminated glass may appear white haze. Solution3:
The combination of pre-laminated glass and roller exhausting air stage
maybe not operate correctly, which lead to Polyvinyl Butyral PVB
interlayer film not reacted perfectly. The main parameters are
temperature, pressure and time. Solution4：
The glass surface is not clean and dry enough. Reason2:
The Polyvinyl Butyral PVB interlayer film is too thin.
Solution:
Use thicker or more layer of Polyvinyl Butyral PVB interlayer film. Reason3:
The plainness of the tempered glass is not good.
Solution: Choose better quality tempered glass. Condition Five: Delamination of Laminated Glass with Polyvinyl Butyral
PVB Interlayer Film When in Boling Water Test Reason1:
Two much air contained inside the laminated glass with Polyvinyl
Butyral PVB interlayer film.
Solution1:
Sealing the edges too early in the pre-pressure exhausting air stage,
which lead to the air stocked inside the laminated glass. Although, it
seams successful when the laminated glass come out from the autoclave,
but when in the boiling test, the bubbles will appears.
Reason2:
The Polyvinyl Butyral PVB interlayer film has absorbed too much
moisture before laminating.
Solution2:
Adjust the storage conditions, make sure the moisture of Polyvinyl
Butyral PVB interlayer film is less than 0.55%. Copyright: All rights reserved by CNC-INTERLAYER TECH:
【1】CNC-Force® EVA INERLAYER FOR ARCHITECTURAL LAMINATED GLASS
【2】CNC-Smart® SMART FILM FOR PRIVACY SWITCHABLE GLASS
【3】CNC-Shield® PVB INTERLAYER FOR AUTOMOTIVE WINDSHIELD GLASS
Mail: [email protected]
Web: www.CNCnext.com
[email protected]/
[email protected]